Wear resistant steel plate in Japan: can be used to manufacture the highest quality equipment and spare parts and to maximize their service life and minimize the risk of failure to maximize production capacity.
JFE-EH400 wear-resistant steel used in the manufacture of bucket loaders, dump trucks, crushers, classifiers, chute, and a variety of wear-resistant liner. JFE-EH400 withstand any form of wear-resistant steel, wear resistant steel plate imports from a variety of rock, sand and gravel wear JFE-EH400 with good workability
Chemical Composition
Type | Grade | Available | Heat Treatment | Chemical Composition(%)* | |||||||||
C | Si | Mn | P | S | Cr | Mo | V | Ti | B | ||||
Standard | JFE-EH360 | 6~50 | Controlled | 0.20 | 0.55 | 1.60 | 0.03 | 0.03 | 0.40 | - | - | 0.005~0.02 | 0.004 |
JFE-EH400 | 0.25 | 0.80 | |||||||||||
JFE-EH500 | 0.35 | 0.80 | |||||||||||
Alloyed | JFE-EH360A | 6~100 | Controlled | 0.20 | 0.55 | 1.60 | 0.03 | 0.03 | 0.40~1.20 | 0.10~0.50 | 0.10 | 0.02 | 0.004 |
JFE-EH500A | 0.35 max |
*Elements that are not given in the above table may be added.
Chemical composition data are quoted from our molten steel analysis.
**Ceq=C + Mn/6 + (Cu+Ni)/15 + (Cr+Mo+V)/5
Mechanical Properties
Type | Grade | Hardness test* | Charpy impact test | |||
Thickness (mm) | Brinell Hardness (3000) | Thickness | Test Temperature | Impact Value J (Average of 3 specimens) | ||
Standard | JFE-EH360 | 6~50 | 361min | - | - | - |
JFE-EH400 | 6~50 | 401min | - | - | - | |
JFE-EH500 | 6~50 | 477min | - | - | - | |
Alloyed | JFE-EH360A | 6~100 | 361min | 13.1~50.0 | 0 | 21min |
JFE-EH500A | 6~100 | 477min | 13.1~25.0 | 0 | 21min |
*Test for plate surface