Excellent Durability:Wear-resistant steel grades such as NM400TUF and NM500TUF have hardness ranging between 370 HBW and 500 HBW (Brinell hardness). This can increase surface hardness and durability, extending product life up to 4 times that of conventional structural steels in high-wear environments, reducing replacement frequency and costs.
High Toughness: GNEE’s high-toughness steels have excellent impact resistance, with Charpy V-notch impact values exceeding 40 J/cm² at temperatures as low as -40°C. This level of impact toughness helps resist cracking and chipping under heavy loads, providing reliable performance even in sub-zero conditions.
Lightweight and High Strength:The yield strength is 700–1300 MPa, depending on the grade, while maintaining a small material thickness. This can reduce part weight by 50% compared to conventional steels with a yield strength of 345 MPa.
Customizable Options:Thicknesses range from 3mm to 25mm to accommodate a wide range of industrial applications, from thin sheets for car bodies to thick plates for wear parts in heavy machinery.
Chemical Composition
Element | NM 400 Tuf (%) | NM 450Tuf (%) | NM 500 Tuf (%) |
Carbon (C) | 0.18-0.26 | 0.20-0.28 | 0.25-0.30 |
Manganese (Mn) | 1.2-1.5 | 1.3-1.6 | 1.4-1.7 |
Chromium (Cr) | 0.5-1.0 | 0.6-1.1 | 0.7-1.2 |
Applications
Construction and Mining Equipment: Ideal for wear-prone parts like excavator buckets, loader dump beds, and crusher liners, where reliability and long life are essential.
Automotive Manufacturing: Commonly used for dump truck bodies, offering reduced weight and energy savings compared to conventional steel grades.
Heavy-Duty Structural Applications: Suitable for framework and support structures requiring superior load-bearing capacity and resistance to harsh environmental conditions.